氧化膜对于铝板的质量有很大的影响。氧化膜就是指铝板在生产的过程中的厚度、孔隙率、透明度等。铝板中膜层的厚度保持在10um以上就可以了,孔隙率以及透明度,这样就可以得到比较好的染色质量。
The oxide film has great influence on the quality of aluminum plate. Oxide film refers to the thickness, porosity and transparency of aluminum sheet in the process of production. Aluminum plate in the film thickness to maintain more than 10 um on it, porosity and transparency, so you can get better dyeing quality.
染色的温度
Dyeing temperature
铝板在染色的过程中分为冷染与热染。使用冷染,所耗费的时间比较长,在染色的过程中期色彩的均匀性比较好掌握。热染使用时间比较短,但是在染色的过程中对于颜色的操控比较难。热染的温度通常在10-60℃。如果在染色的过程中,温度过高,会减小染色的吸附性,并且容易导致铝板表面发花。
The aluminum plate is dyed in cold and heat. The use of cold dyeing, the time spent is longer, in the process of dyeing the color uniformity of the middle better grasp. The use of heat dyes is relatively short, but it is difficult to control the color in the dyeing process. The temperature of heat dyeing is usually 10-60 degrees. If the temperature is too high in the process of dyeing, it will reduce the adsorption of dyeing, and easily lead to the surface of aluminium plate flower.
铝板制件原料的影响
Influence of raw materials on aluminum sheet
通常大家在生产的过程中高纯铝、铝镁、铝锰合金经过阳极氧化以后,其中染色的功能是最好的,可以染成各种各样的颜色。对于含有硅或铜比较重的板材,在染色的过程中只能够染成深色与黑色,比较单调的颜色。
Usually we in the production process of high-purity aluminum, aluminum magnesium, aluminum manganese alloy after anodizing, of which the function of dyeing is the best, can be dyed into a variety of colors. For heavy plates containing silicon or copper, the dyeing process can only be dyed dark and black, relatively monotonous color.
染色液浓度

铝卷生产厂家
Dyeing solution concentration
铝板的浓度与染色之间存在一定的联系,如果铝板染成淡色,其中浓度可以降低一点,染成深色浓度可以高一点。
There is a certain relationship between the concentration of aluminum plate and dyeing, if the aluminum plate dyed light, the concentration can be reduced a little, dyed dark concentration can be higher.
通常所生产的铝板材料所染比较淡的颜色其色彩为0.1-0.39g/L,染淡色彩为1g/L,染深色彩为3-5g/L,染稠密的色彩为10-15g/L,如果要求的染色浓度比较高就会造成颜色不均或者会出现浮色的现象,在清洁与关闭的过程汇总容易产生流色。
Usually the lighter colors of the aluminum sheet materials are 0.1-0.39g/L, 1g/L, 3-5g/L, and 10-15g/L. If the required dyeing concentration is high, the color will be uneven or float, and flow will easily occur during the cleaning and closing process. Color.
为了加强其染色的吸附性能,这样可以使用低浓度颜色进行延伸染色,这样可以使染料能够比较均匀的渗透到氧化膜中,这样可以使染色更加和谐与牢固。
In order to enhance its dyeing adsorption performance, this can use low concentration of color for extended dyeing, so that the dye can be more uniform penetration into the oxide film, this can make the dyeing more harmonious and firm.